. S. Khani, . M. T. Salehi, . H. R. Samim, Prof. M. R. Aboutalebi, . H. Palkowski,
Volume 13, Issue 3 (9-2016)
Abstract
The evolution of microstructure and mechanical properties of a magnesium cast alloy (AZ31) processed by equal channel angular pressing (ECAP) at two different temperatures were investigated. The as-cast alloy with an average grain size of 360 was significantly refined to about 5 after four ECAP passes at 543 K. Grain refinement was achieved through dynamic recrystallization (DRX) during the ECAP process in which the formation of necklace-type structure and bulging of original grain boundaries would be the main mechanisms. ECAP processing at lower temperature resulted in finer recrystallized grains and also a more homogenous microstructure. The mechanical behavior was investigated at room temperature by tensile tests. The obtained results showed that the ECAP processing can basically improve both strength and ductility of the cast alloy. However, the lower working temperature led to higher yield and ultimate strength of the alloy.
A. Eivani, S.h. Seyedein, M. Aboutalebi,
Volume 15, Issue 1 (3-2018)
Abstract
In this research, samples of AlMg0.7Si aluminum alloy are deformed up to three passes using equal channel angular pressing (ECAP). Formation of a sub-micron structure after three passes of ECAP is demonstrated. Microstructural stability of the samples is investigated at temperatures of 300-500 °C. At 300 °C, fine recrystallized structure forms after 10 min which remains stable when the annealing proceeds up to 18 hrs. However, at 350 °C and higher, the microstructure is quite unstable. Even by 10 sec annealing, the samples exhibit recrystallized structure which turned to abnormal grain growth when temperature enhances to 500 °C and time up to 300 sec.
Gajanan M Naik, Santhosh Kumar B M, Shivakumar M M, Ramesh S, Maruthi Prashanth B H, Gajanan Anne6,
Volume 22, Issue 3 (9-2025)
Abstract
Magnesium and the alloys made from the same metal are utilized in the engineering applications such as automotive, marine, and aircraft, among others due to high strength to weight. Nevertheless, the applications of magnesium alloys are currently limited to a certain level due to their poor wear and corrosion properties. Another effective strategy for enhancing these properties involves utilizing the process of equal channel angular extrusion (ECAE), which serves to refine the grain structure, thereby resulting in improved material properties. This paper aims to establish the relationship between grain size reduction and wear and corrosion of AZ91 alloy. The wear performances of both coarse-grained and fine-grain alloy were conducted using L9 orthogonal array of experiments in order to study the effects of control parameters on wear performance. In the study, it has also been identified that through ECAP, the corrosion barrier and wear characteristics of the alloy were enhanced due to fine-grain-structure and the spheroidal precipitation of the second β-phase particles. Further, the influence of these changes on the performance of the AZ91 Mg alloy was assessed using SEM.